The paper presents the outcomes of experimental research within the scope of formation of cumbersome aluminum primarily based composite supplies (CM) with carbon nanofibers (CNF), together with the analysis strategies of sizzling extrusion and rolling. Extrusion manufacture of cumbersome composite supplies contributes to acquire billets with a minimal compression diploma (λ = 1.5). To scale back shear deformations and formation of pores in extruded billet, the extrusion course of modes have been chosen experimentally. In the midst of additional rolling operation, mechanical properties improve twice and inhomogeneity is compensated after important compression of the extrusion billets, and the shear deformations are diminished in full quantity of the fabric. Cumbersome supplies achieve excessive hardness, put on resistance and energy. The economically alloyed composite materials has possible prospects to be relevant in light-weight constructions for aviation and vehicle industries.